This set of Foundry Technology Multiple Choice Questions & Answers (MCQs) focuses on Foundry Technology Set 11
Q1 | Pattern draft for internal surfaces is (in mm/m)
- 10 -- 30
- 50 - 80
- 40 - 70
Q2 | On drying the shrinkage of wood is least
- along the grains
- across the grains
- along the direction of tangent to the annular rings
Q3 | Contraction of metal starts at the end of
- mushy stage
- plastic stage
- liquid stage
- solid stage
Q4 | In radiography test on castings which of the following rays are never used?
- X-rays
- beta rays
- gamma rays
- all of the above
Q5 | Metal moulds are used in
- dry sand moulding
- green sand moulding
- die casting process
- loam moulding
Q6 | The defect known as 'drop' occurs when the upper surface of the mould cracks and pieces of sand fall into the molten metal. This defect occurs due to
- low mould hardness
- insufficient reinforcement
- low green strength
- any of the above
Q7 | Investment casting finds application in all of the following EXCEPT
- Jet engine nozzles
- Milling cutters
- Buckets for superchargers
- Gold ornaments
Q8 | Lowest pouring temperature alloy is
- Phosphor bronze
- Cupro nickel alloy
- Monel metal
- Tin bronze
Q9 | The residual stresses in casting occur due to
- sand particles being taken into molten metal while pouring
- the insufficient gate size
- the differential solidification rate of thin and thick sections of casting
- none of the above
Q10 | Local stress relief treatments are generally given to
- small castings
- non-ferrous castings
- all castings
- too large castings
Q11 | Which of the following is used on moulds for magnesium castings to prevent metal mould reactions?
- Boric sulphur
- Molasses
- Charcoal
- all of the above
Q12 | Silica is the second most important constituent of moulding sand which provides
- binding strength
- refractoriness
- chemical resistance
- none of the above
Q13 | Flash occurs on diecastings at the
- gatting system
- ejection pins
- vents between the dies
- parting surface of two dies
Q14 | The methods of casting for producing ornamental pieces are
- pressed and slush casting
- slush and gravity casting
- gravity and semi permanent mould casting
- none of the above