Q1 | Which of the following is usually made of dead mild steel?
- Flanges
- Shafts
- Spades
- Gears
- Fish plates
Q2 | The fastest cooling rate is achieved when steel is quenched in
- Brine
- Soldering
- Oil
- Water
- Air
Q3 | An operation on steel aimed at softening the steel to improve machinability is known as
- Annealing
- Cold working
- Softening
- Temperature
- Shot blasting
Q4 | Which of the following material can bear sudden and excessive shocks better?
- White iron
- Pig iron
- Wrought iron
- All have same shock bearing capacity
- Cast iron
Q5 | The process for steel making used at TISCO, Jamshedpur is
- Duplex process
- Open hearth process
- Bessemmer process
- L-D process
- Electric process
Q6 | In Brinell hardness testing the minimum thickness of the specimen should be
- More than 10 times the depth of impression
- Less than 10 times the depth of impression
- Less than 5 times the depth of impression
- Thickness of specimen has no relevance to the depth of impression
- Equal to 10 times the depth of impression
Q7 | Vicker's hardness number of diamond could be of the order of
- 8000
- 800
- 4000
- 15000
- 12000
Q8 | Carbon percentage in cutlery stainless steel is
- 1.35 to 1.65 percent
- 1.1 to 1.35 percent
- 1 percent
- 0.76 to 0.80 percent
- 0.25 to 0.30 percent
Q9 | The crystal structure of gamma iron is
- BCC
- Combination of all above
- ACP
- Cubic
- FCC
Q10 | High carbon steels intended to be quenched in water should have manganese percentage less than
- 1.5 percent
- 0.5 percent
- 2 percent
- 1 percent
- No manganese percent
Q11 | A fine grained steel will have the number of grains per square centimeter as
- 100 to 150
- 150 to 1000
- 16 to 56
- 3 to 16
- 56 to 100
Q12 | Uniformity of zinc coating on pipes is tested by
- Dipping the sample in water
- Dipping the sample for 10 minutes in calcium hydroxide solution
- Dipping the sample for 1 minute in conc, hydrochloric acid
- Dipping the sample for 1 minute in neutral copper sulphate solution
- By passing electric current for 1 hour
Q13 | Which of the following materials are usually most ductile?
- Amorphous
- Face centred cubic lattice
- Non-metallic
- Body centred lattice
- Hexagonal close-packed lattice
Q14 | In grey cast iron, free graphite is in the form of
- Fine powder
- Needles
- Nodules
- Crystals
- Flakes
Q15 | Volume of air required to melt one ton of cast iron in a cupola at N.T.P. is roughly
- 10000 cubic metres of air
- 10 cubic metres of air
- 100000 cubic metres of air
- 100 cubic metres of air
- 1000 cubic metres of air
Q16 | The property of a metal when the recovery after unloading is complete but not instantaneous is
- 9
- Viscoelasticity
- Inelasticity
- Anelasticity
- creep
Q17 | Standard electrical resistance are made of
- Invar
- Manganin
- Tungsten
- Phosphor bronze
- Constantan
Q18 | A chisel for cutting steel plates is usually
- Hardened and tempered
- Annealed
- Hardened
- Tempered
- Tempered and annealed
Q19 | Cracks of a vertical nature and dark coloured fissures in a sample of hardened steel indicate that
- Steel has not been properly heated
- Steel has been burned
- Steel contains excessive alloying elements
- Steel has been properly hardened
- Steel has achieved maximum possible hardness in accordance with the carbon percentage
Q20 | Which of the following material is viscoelastic in properties?
- Graphite
- Rubber
- Glass
- Cork
- None of the above
Q21 | Brinell hardness of nitrided surface may be of the order of
- More than 600
- 200 to 250
- 300 to 450
- 150 to 200
- 100
Q22 | If a medium carbon hardened steel shows pearlite structure it may be concluded that
- Steel contains impurities
- Presence of cementite
- Steel has been quenched in oil
- Steel has been quenched in water
- Steel has been slowly cooled in furnace
Q23 | Alpha brass is a (an)
- Inermediate phase
- Interstitial compound
- Substitutional solid solution
- None of the above
- 2.10%
Q24 | Which of the following is a non-destructive test?
- Tensile test
- Cupping test
- Charpy test
- X-ray test
- Izod Impact test
Q25 | For each ton of pig iron produced in blast furnace, the quantity of coke required would be roughly
- 0.5 ton
- 0.25 ton
- 1.4 ton
- 1.9 ton
- 0.1 ton